37 Hole Checker Brick Low Creep For Steel plant hot blast stove
Silicon Mullite Wear-Resistant brick is made from super high bauxite clinker and silicon carbide as main raw materials by high pressure forming and high temperature firing. The product has high compressive strength at room temperature and high temperature structural strength, good thermal shock stability, continuous formation of protective layer during use, good wear resistance, strong resistance to spalling, suitable for cement kiln transition belt, cooling belt, kiln mouth and other parts.
▌FEATURES
1. Low creep rate；
2. High mechanical strength；
3. Good abrasive resistance；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
DRN-125 |
DRN-120 |
DRN-115 |
DRN-110 |
|
|
Chemical composition |
Al2O3 |
% |
≥45 |
≥42 |
≥40 |
≥36 |
|
Apparent Porosity |
% |
≤22(24) |
≤22(24) |
≤22(24) |
≤22(24) |
|
|
Bulk Density |
g/cm3 |
≥2.15-2.35 |
≥2.00-2.20 |
≥2.00-2.20 |
≥2.00-2.20 |
|
|
Cold Crushing Strength |
MPa |
≥40 |
≥35 |
≥30 |
≥25 |
|
|
Heating Permanent Line Change |
% |
1400℃*2h -0.3~0.1 |
1350℃*2h -0.3~0.1 |
1300℃*2h -0.4~0.1 |
1300℃*2h -0.4~0.1 |
|
|
Creep Rate(0.2MPa) |
% |
1250*50h ≤0.8 |
1200*50h ≤0.8 |
1150*50h ≤0.8 |
1150*50h ≤0.8 |
|
▌PRODUCT PICTURE
Video
|
|
| Brand Name: | Jansincere |
| MOQ: | Negotiable |
| Price: | Negotiable |
| Packaging Details: | Depends on equipment sizes |
| Payment Terms: | L/C,D/A,D/P,T/T,Western Union,MoneyGram |
37 Hole Checker Brick Low Creep For Steel plant hot blast stove
Silicon Mullite Wear-Resistant brick is made from super high bauxite clinker and silicon carbide as main raw materials by high pressure forming and high temperature firing. The product has high compressive strength at room temperature and high temperature structural strength, good thermal shock stability, continuous formation of protective layer during use, good wear resistance, strong resistance to spalling, suitable for cement kiln transition belt, cooling belt, kiln mouth and other parts.
▌FEATURES
1. Low creep rate；
2. High mechanical strength；
3. Good abrasive resistance；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
DRN-125 |
DRN-120 |
DRN-115 |
DRN-110 |
|
|
Chemical composition |
Al2O3 |
% |
≥45 |
≥42 |
≥40 |
≥36 |
|
Apparent Porosity |
% |
≤22(24) |
≤22(24) |
≤22(24) |
≤22(24) |
|
|
Bulk Density |
g/cm3 |
≥2.15-2.35 |
≥2.00-2.20 |
≥2.00-2.20 |
≥2.00-2.20 |
|
|
Cold Crushing Strength |
MPa |
≥40 |
≥35 |
≥30 |
≥25 |
|
|
Heating Permanent Line Change |
% |
1400℃*2h -0.3~0.1 |
1350℃*2h -0.3~0.1 |
1300℃*2h -0.4~0.1 |
1300℃*2h -0.4~0.1 |
|
|
Creep Rate(0.2MPa) |
% |
1250*50h ≤0.8 |
1200*50h ≤0.8 |
1150*50h ≤0.8 |
1150*50h ≤0.8 |
|