Jianxin Fire Resistant Lightweight Refractory Bricks High Alumina Insulation Brick Insulating Brick NG-1.0
Clay heat insulation brick is made of fire clay as the main raw material of AL2O3 content of 30%-48% heat insulation refractory products. The production process adopts burnt-out additive method and foam method. The product with bulk density of 0.3-1.5g/cm3 was prepared by using fireclay, bleach bead and fireclay clinker as raw materials, adding binder and sawdust, mixing, forming, drying and firing.
▌FEATURES
1. Low thermal conductivity；
2. High mechanical strength；
3. Good insulation effect；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
NG-0.8 |
NG-1.0 |
LG-0.8 |
LG-1.0 |
|
|
Chemical composition |
Al2O3 |
% |
≥75 |
≥75 |
≥65 |
≥65 |
|
Apparent Porosity |
% |
≤20 |
≤21 |
≤21 |
≤22 |
|
|
Bulk Density |
g/cm3 |
≥2.65-2.85 |
≥2.65-2.85 |
≥2.50-2.70 |
≥2.40-2.60 |
|
|
Cold Crushing Strength |
MPa |
≥60 |
≥60 |
≥60 |
≥55 |
|
|
Permanent Linear Change |
% |
1550℃*2h -0.2~0.1 |
1550℃*2h -0.2~0.1 |
1550℃*2h -0.2~0.1 |
1450℃*2h -0.2~0.1 |
|
|
Creep Rate(0.2MPa,50h) |
% |
1550℃ ≤0.8 |
1500℃ ≤0.8 |
1450℃ ≤0.8 |
1400℃ ≤0.8 |
|
▌PRODUCT PICTURE
Video
Video
|
|
| Brand Name: | Jansincere |
| Model Number: | T-3/T-38 |
| MOQ: | Negotiable |
| Price: | Negotiable |
| Packaging Details: | Depends on equipment sizes |
| Payment Terms: | L/C,D/A,D/P,T/T,Western Union,MoneyGram |
Jianxin Fire Resistant Lightweight Refractory Bricks High Alumina Insulation Brick Insulating Brick NG-1.0
Clay heat insulation brick is made of fire clay as the main raw material of AL2O3 content of 30%-48% heat insulation refractory products. The production process adopts burnt-out additive method and foam method. The product with bulk density of 0.3-1.5g/cm3 was prepared by using fireclay, bleach bead and fireclay clinker as raw materials, adding binder and sawdust, mixing, forming, drying and firing.
▌FEATURES
1. Low thermal conductivity；
2. High mechanical strength；
3. Good insulation effect；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
NG-0.8 |
NG-1.0 |
LG-0.8 |
LG-1.0 |
|
|
Chemical composition |
Al2O3 |
% |
≥75 |
≥75 |
≥65 |
≥65 |
|
Apparent Porosity |
% |
≤20 |
≤21 |
≤21 |
≤22 |
|
|
Bulk Density |
g/cm3 |
≥2.65-2.85 |
≥2.65-2.85 |
≥2.50-2.70 |
≥2.40-2.60 |
|
|
Cold Crushing Strength |
MPa |
≥60 |
≥60 |
≥60 |
≥55 |
|
|
Permanent Linear Change |
% |
1550℃*2h -0.2~0.1 |
1550℃*2h -0.2~0.1 |
1550℃*2h -0.2~0.1 |
1450℃*2h -0.2~0.1 |
|
|
Creep Rate(0.2MPa,50h) |
% |
1550℃ ≤0.8 |
1500℃ ≤0.8 |
1450℃ ≤0.8 |
1400℃ ≤0.8 |
|