Wear-Resistant Special Unburned Phosphate Brick For Lime Kiln
Phosphate bonded high alumina bricks are made from high alumina bauxite aggregate, selecting phosphoric acid or aluminum phosphate as binder. Finished phosphate bonded high alumina brick must go through 400~600 ℃ heating process and semi-dry compress process. Featured by high wear-resistance, high refractoriness and good thermal shock resistance, phosphate bonded high alumina bricks are widely used in rotary cement and lime kiln transition zone, sintering zone, cooling zone and cooler working layer.
▌FEATURES
1. High mechanical strength；
2. Good spalling resistanceh；
3. Good wear resistance；
4.Good thermal shock resistance；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
PA-2.80 |
PA-2.85 |
PA-2.90 |
|
|
Chemical composition |
Al2O3 |
% |
≥72 |
≥75 |
≥77 |
|
Fe2O3 |
% |
≤3.2 |
≤3.2 |
≤3.2 |
|
|
Apparent Porosity |
% |
≤18 |
≤17 |
≤17 |
|
|
Bulk Density |
g/cm3 |
≥2.80 |
≥2.85 |
≥2.90 |
|
|
Cold Crushing Strength |
MPa |
≥80 |
≥90 |
≥90 |
|
|
Refractoriness Under load |
℃ |
≥1450 |
≥1500 |
≥1550 |
|
|
Thermal Shock Resistance(Water) |
Cycles |
≥8 |
≥10 |
≥12 |
|
▌PRODUCT PICTURE
|
|
| Brand Name: | Jansincere |
| Model Number: | 422/622 |
| MOQ: | Negotiable |
| Price: | Negotiable |
| Packaging Details: | Depends on equipment sizes |
| Payment Terms: | L/C,D/A,D/P,T/T,Western Union,MoneyGram |
Wear-Resistant Special Unburned Phosphate Brick For Lime Kiln
Phosphate bonded high alumina bricks are made from high alumina bauxite aggregate, selecting phosphoric acid or aluminum phosphate as binder. Finished phosphate bonded high alumina brick must go through 400~600 ℃ heating process and semi-dry compress process. Featured by high wear-resistance, high refractoriness and good thermal shock resistance, phosphate bonded high alumina bricks are widely used in rotary cement and lime kiln transition zone, sintering zone, cooling zone and cooler working layer.
▌FEATURES
1. High mechanical strength；
2. Good spalling resistanceh；
3. Good wear resistance；
4.Good thermal shock resistance；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
PA-2.80 |
PA-2.85 |
PA-2.90 |
|
|
Chemical composition |
Al2O3 |
% |
≥72 |
≥75 |
≥77 |
|
Fe2O3 |
% |
≤3.2 |
≤3.2 |
≤3.2 |
|
|
Apparent Porosity |
% |
≤18 |
≤17 |
≤17 |
|
|
Bulk Density |
g/cm3 |
≥2.80 |
≥2.85 |
≥2.90 |
|
|
Cold Crushing Strength |
MPa |
≥80 |
≥90 |
≥90 |
|
|
Refractoriness Under load |
℃ |
≥1450 |
≥1500 |
≥1550 |
|
|
Thermal Shock Resistance(Water) |
Cycles |
≥8 |
≥10 |
≥12 |
|
▌PRODUCT PICTURE