High Temperature Kiln Castable Refractory Cement Quick-Drying Explosion-Proof Castable
High aluminum castable is high aluminum aggregate with AL2O3 content greater than 75% as particle raw materials, combined with high aluminum powder and admixture composed of the overall aluminum content > 55% of the amorphous refractory castable, high aluminum castable after the initial solidification, standard curing to 28d, compressive strength up to 40~60MPa. It is characterized by slow hydration rate, high late strength and high refractoriness.
▌FEATURES
1. High refractoriness under load；
2. High compressive strength；
3. Good abrasive resistance ；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
Jans-75C |
||
|
Chemical composition |
Al2O3 |
% |
≥75 |
|
|
Fe2O3 |
% |
≤1.8 |
||
|
Bulk Density |
g/cm3 |
≥2.30 |
||
|
Cold Crushing Strength |
110℃*24h |
MPa |
≥70 |
|
| 1100℃*3h | MPa | ≥85 | ||
|
Modules of Rupture |
110℃*24h | MPa | ≥6 | |
| 1100℃*3h | MPa | ≥8 | ||
|
Refractoriness Under load |
℃ |
≥1450 |
||
|
Reheating Linear Change |
% |
1300*3h -0.1~+0.1 |
||
▌PRODUCT PICTURE
|
|
| Brand Name: | Jansincere |
| MOQ: | Negotiable |
| Price: | Negotiable |
| Packaging Details: | Depends on equipment sizes |
| Payment Terms: | L/C,D/A,D/P,T/T,Western Union,MoneyGram |
High Temperature Kiln Castable Refractory Cement Quick-Drying Explosion-Proof Castable
High aluminum castable is high aluminum aggregate with AL2O3 content greater than 75% as particle raw materials, combined with high aluminum powder and admixture composed of the overall aluminum content > 55% of the amorphous refractory castable, high aluminum castable after the initial solidification, standard curing to 28d, compressive strength up to 40~60MPa. It is characterized by slow hydration rate, high late strength and high refractoriness.
▌FEATURES
1. High refractoriness under load；
2. High compressive strength；
3. Good abrasive resistance ；
▌PHYSICAL AND CHEMICAL INDICATORS
|
Item |
Unit |
Jans-75C |
||
|
Chemical composition |
Al2O3 |
% |
≥75 |
|
|
Fe2O3 |
% |
≤1.8 |
||
|
Bulk Density |
g/cm3 |
≥2.30 |
||
|
Cold Crushing Strength |
110℃*24h |
MPa |
≥70 |
|
| 1100℃*3h | MPa | ≥85 | ||
|
Modules of Rupture |
110℃*24h | MPa | ≥6 | |
| 1100℃*3h | MPa | ≥8 | ||
|
Refractoriness Under load |
℃ |
≥1450 |
||
|
Reheating Linear Change |
% |
1300*3h -0.1~+0.1 |
||